It uses some low-cost raw materials, has a high cost performance, is suitable for medium-temperature 130℃ co-curing process, and has excellent medium-temperature resistance to compression deformation; with special heat treatment and quality control, it can be adapted to 150℃ co-curing process.
Keywords: Zihafoam Medium-Temperature PMI Foam
Category: PMI Foam Products
It uses some low-cost raw materials, has a high cost performance, is suitable for medium-temperature 130℃ co-curing process, and has excellent medium-temperature resistance to compression deformation; with special heat treatment and quality control, it can be adapted to 150℃ co-curing process.It has been successfully applied in civilian fields such as medical devices and sports equipment.
| Typical density (kg/m³) | Model | Room Temperature Mechanical Properties | Mid-temperature performance at 130℃ | ||||||||||
| Compressive strength (MPa) | compression modulus (MPa) | Tensile strength (MPa) | Tensile modulus (MPa) | Elongation at break (%) | Shear strength (MPa) | Shear modulus (MPa) | Bending strength (MPa) | Flexural modulus (MPa) | Compressive strength (MPa) | compression modulus (MPa) | Dimensional change rate (absolute value) | ||
| Test Standards | GB/T8813-2008 | GB/T7964-1988 | GB/T1455-2005 | GB/T8812.2-2007 | GB/T8813-2008 | GB/T8811-2008 | |||||||
| 52 | FXK52 | 0.9 | 50 | 1.5 | 60 | 2.4 | 0.8 | 23 | 2 | 51 | 0.7 | 30 | 0.6 |
| 75 | FXK75 | 1.5 | 80 | 1.9 | 70 | 2.46 | 1.2 | 36 | 2.3 | 85 | 1 | 50 | 0.6 |
| 110 | FXK110 | 3 | 150 | 3 | 130 | 2.54 | 2.1 | 50 | 4.8 | 145 | 1.4 | 55 | 0.6 |
Antenna Radome
Drones
Sports Equipment
Ships and Yachts
Transportation
Wind Turbine Blades
Phone: +86 18357131518
Email: malin@lhkjjt.com
Address: No. 105, Huanghe Road, Huayang Industrial Agglomeration Zone, Baihe Town, Mengjin District, Luoyang City, Henan Province